Model No.: A517 high strength steel plate

Standard: Aisi, Astm, Bs, Din, Gb, Jis

Place Of Origin: China

Species: Steel Plate

Production Process: Hot Rolled

Special Steel: High-Strength Steel Plate

Tolerance: ±1%

Category: Hot Rolled Steel Sheet, Steel Plate, Low-Alloy Plate

Processing Service: Bending, Welding, Decoiling, Cutting, Punching

Verpakung & Liwwerung

Eenheeten ze verkafen

Ton

The file is encrypted. Please fill in the following information to continue accessing it

Produkt beschreiwung

ASTM A517 Héich Rendus-Stäerkt Steelplack gëtt och Asme SA517 HSLA Stol, wéi eng Referenzen amerikanesche Standarden. A517 / Sa517 héich Kraaft niddereg Legierung ass eng héich Stäerkt, renken an temperéiert Alesserte vun der Fusiounsklasse an aner Drock

Mir kënnen Iech eng 6,717GRD héich Kraaftpolumpole placéieren, a517GR Paller Bladel, a517GPROLLT Highlebh héich Stëmm.

A517 Grad eng héich Stäerkt Algoletting Stahl chemesch Zesummesetzung:

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S
A517 grade A	0.13-0.23	0.34-0.86	0.74-1.20	0.035	0.035
	Cr	Mo	B	Zr
	0.46-0.84	0.15-0.31	0.0025	0.04-0.16

A517 Grad eng Allo-Sankmanesch Eegeschafte:

Grade	Thickness	Yield	Tensile	Elongation
A517 grade A	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

A517 Grad B héich Stäerkt Stol Chemeschen Zesummesetzung:

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S
A517 grade B	0.13-0.23	0.13-0.37	0.64-1.10	0.035	0.035
	Cr	Mo	B	Ti	V
	0.36-0.69	0.12-0.28	0.0005-0.005	0.01-0.05	0.02-0.09

A511177 Graplecholplacke Mäikatum Lëtzebuerg:

Grade	Thickness	Yield	Tensile	Elongation
A517 grade B	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

A517 Grad E Héich Kraaft allegy-Stol Plather chemesch Zesummesetzung:

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S
A517 grade E	0.10-0.22	0.08-0.45	0.35-0.78	0.035	0.035
	Cr	Mo	B	Ti	V
	1.34-2.06	0.36-0.64	0.001-0.005	0.005-0.11

A517 Héichrai Grad iewert Kraaft Emplocitéitputeur:

Grade	Thickness	Yield	Tensile	Elongation
A517 grade E	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

A517 Grad f Héich Stäerkt Legoogen Stahl-chemesche Zesummesetzung:

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S	Cu
A517 grade F	0.08-0.22	0.13-0.37	0.55-1.10	0.035	0.035	0.12-0.53
	Cr	Mo	B	V	Ni
	0.36-0.69	0.36-0.64	0.0005-0.006	0.02-0.09	0.67-1.03

A5177 Grad Fëllt FLLOLOTCHÄR M Meriticelin.

Grade	Thickness	Yield	Tensile	Elongation
A517 grade F	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

A517 Grad H LYLY-Stahllack Chemikalkompositioun:

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S	Ni
A517 grade H	0.10-0.23	0.13-0.37	0.87-1.41	0.035	0.035	0.27-0.73
	Cr	Mo	B	V
	0.36-0.69	0.17-0.33	MIN 0.0005	0.02-0.09

A51777 CA HSla SDATIK Merschénger:

Grade	Thickness	Yield	Tensile	Elongation
A517 grade H	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

A517 Grad p niddereg alloye Stol chemesche Zesummesetzung:

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S	Ni
A517 grade P	0.10-0.23	0.18-0.37	0.40-0.78	0.035	0.035	1.15-1.55
	Cr	Mo	B
	0.79-1.26	0.41-0.64	0.001-0.005

A51 playp-Leidenbolde Balifikatioun:

Grade	Thickness	Yield	Tensile	Elongation
A517 grade P	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

A517 Grad Q Niddereg Alyloy Stolplatigel chemesch Zesummesetzung:

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S	Ni
A517 grade Q	0.12-0.23	0.13-0.37	0.87-1.41	0.035	0.035	1.15-1.55
	Cr	Mo	V
	0.94-1.56	0.36-0.64	0.02-0.09

A517 Grad Q héich Kraaftziel Gottical

Grade	Thickness	Yield	Tensile	Elongation
A517 grade Q	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

AXPL-Claude klanzeg Mangel

Grade	The Element Max (%)
Grade	C	Si	Mn	P	S	Ti
A517 grade S	0.10-0.22	0.13-0.45	1.02-1.62	0.035	0.035	0.07
	Cb	Mo
	0.07	0.10-0.38

A517 Grad déckglëmmert niddereg Strukturell Strukturkéiersmecheschafte:

Grade	Thickness	Yield	Tensile	Elongation
A517 grade S	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%